مدل شماره: Q235A Q235B Q235C Q235D
نام تجاری: هیومینگ
Standard: Gb
Place Of Origin: China
Species: Steel Plate
Production Process: Hot Rolled
Surface Treatment: Coated, Galvanized
کاربرد: Container Plate, Flange Plate, Ship Plate
Special Steel: High-Strength Steel Plate, low alloy carbon steel
Tolerance: ±1%
Category: Hot Rolled Steel Sheet, Steel Plate, Low-Alloy Plate
Processing Service: Bending, Welding, Decoiling, Cutting, Punching, Bending Welding Decoiling
حمل و نقل: Ocean,Land
محل منبع: چین
بندر: qingdao,tianjin,shanghai
نوع پرداخت: L/C,T/T,D/P,D/A
اینکوترم: FOB,CFR,CIF,EXW
| GB/T700 Q235A | |||||
| C% | Si % | Mn % | P% | S% | N% |
| 0.23-0.24 | 0.6 | 1.7 | 0.035 | 0.035 | ... |
| Thickness | Yield Strength (Mpa) | Tensile Strength | Elongation | Impact Energy | |
| (mm) | (MPa) | % | Min | ||
| ≤16 | 235 | 370-500 | 26 | 20 | 27J |
| ＞16 - 40 | 225 | 370-500 | 25 | 20 | 27J |
| ＞40 | 215 | 370-500 | 24 | 20 | 27J |
| The min impact energy is longitudinal energy | |||||
| GB-T700 Q235B | |||||
| C% | Si % | Mn % | P% | S% | N% |
| 0.22 | 0.35 | 1.4 | 0.045 | 0.025 | ... |
| Thickness | Yield Strength (Mpa) | Tensile Strength | Elongation | Impact Energy | |
| (mm) | (MPa) | (%) | Min | ||
| ≤16 | 235 | 370-500 | 26 | 20 | 27J |
| ＞16 - 40 | 225 | 370-500 | 25 | 20 | 27J |
| ＞40 | 215 | 370-500 | 24 | 20 | 27J |
| The min impact energy is longitudinal energy | |||||
| GB-T700 Q235C | |||||
| C% | Si % | Mn % | P% | S% | N% |
| ≤0.17 | ≤0.35 | ≤1.4 | ≤0.040 | ≤0.040 | ... |
| Thickness | Yield Strength (Mpa) | Tensile Strength | Elongation | Impact Energy | |
| (mm) | (MPa) | (%) | Min | ||
| ≤16 | 235 | 370-500 | 26 | 0 | 27J |
| ＞16 - 40 | 225 | 370-500 | 25 | 0 | 27J |
| ＞40 | 215 | 370-500 | 24 | 0 | 27J |
| The min impact energy is longitudinal energy | |||||
| GB-T700 Q235D | |||||
| C% | Si% | Mn % | P% | S% | N% |
| 0.17 | 0.35 | 1.4 | 0.035 | 0.035 | ... |
| Thickness | Yield Strength (Mpa) | Tensile Strength | Elongation | Impact Energy | |
| (mm) | (MPa) | (%) | Min | ||
| ≤16 | 235 | 370-500 | 26 | 0 | 27J |
| ＞16-40 | 225 | 370-500 | 25 | 0 | 27J |
| ＞40 | 215 | 370-500 | 24 | 0 | 27J |
| The min impact energy is longitudinal energy | |||||